Type: | Graphite Mold |
---|---|
Composition: | Petroleum Coke and Tar Coke. |
Carbon Content: | High-Carbon |
Grade: | Industrial Grade |
Forming Way: | Isostatic Graphite |
Crystal Morphology: | Artificial Graphite |
Customization: |
---|
Suppliers with verified business licenses
TYPES | APPARENTDENSITY | ELECTRICALRESISTIVITY | THERMAL CONDUCTIVITY (100ºC) | (-600ºC)COFFICIENT OF THE RMALEXPANSION (ROOM TEMPERATURE-600ºC) | SHORE HARDNESS | FLEXURAL STERENGTH | COMPRESSIVE STRENGTH | MODULUS OF ELASTICITY | POROSITY | ASH | PURIFY THE ASH | PARTICLE SIZE | |
g/cm³ | μΩm | W/mk | 10-6/ºC | HSD | Mpa | Mpa | Gpa | % | PPM | PPM | micron | ||
wh-4 | 1.75 | 8~11 | 121.1 | 5.46 | 42 | 38 | 65 | 9 | 17 | 500 | 50 | 13~15 | |
wh-5 | 1.85 | 8~10 | 139.2 | 4.75 | 48 | 46 | 85 | 11.8 | 13 | 500 | 50 | 13~15 | |
whd-5 | 1.68 | 13 | 90 | 5 | 51 | 38 | 86 | 8.8 | 18 | 500 | 50 | 13~15 | |
wh-10 | 1.75 | 12~14 | 85 | 5.5 | 56 | 41 | 85 | 10.3 | 16 | 500 | 50 | 12 | |
whh-6 | 1.88 | 8~9 | 140 | 5.1 | 53 | 55 | 95 | 12 | 11 | / | 50 | 8~10 | |
wh-7 | 1.85 | 11~13 | 85 | 5.6 | 65 | 51 | 115 | 11 | 12 | 500 | 50 | 8~10 | |
wh-8 | 1.91 | 11~13 | 85 | 5.85 | 70 | 60 | 135 | 12 | 11 | 500 | 50 | 8~10 |